Synthesis and characterization of water soluble polymer stabilized transition metal(0) nanoclusters as catalyst in hydrogen generation from the hydrolysis of sodium borohydride and ammonia borane


Tezin Türü: Doktora

Tezin Yürütüldüğü Kurum: Orta Doğu Teknik Üniversitesi, Fen Edebiyat Fakültesi, Kimya Bölümü, Türkiye

Tezin Onay Tarihi: 2010

Öğrenci: ÖNDER METİN

Danışman: SAİM ÖZKAR

Özet:

Metal nanoclusters exhibit unique properties which differ from their bulk materials, owing to the quantum size effects. For example, the catalytic activity of transition metal nanoclusters generally increases with decreasing particle size. However, nanoclusters tend to be fairly unstable with respect to the agglomerate into bulk metal in solution and thus special precautions have to be taken to avoid their aggregation or precipitation during the preparation of such nanoclusters in solution. In order to obtain stable nanoclusters dispersed in solution, a stabilizing agent is usually added into the reaction system. The stabilization of metal nanoclusters in solution can be achieved either by electrostatically by using charged ions such as acetate ion or sterically by long chain molecules such as polymers. Polymers are one of the most widely used steric stabilizers for the preparation of stable metal nanoclusters in solution. The use of polymers as stabilizer for the synthesis of transition metal nanoclusters provides advantegous regarding solubility, conductivity, thermal stability and reusability. The metal nanoclusters stabilized by polymers generally show higher catalytic activity, stability and optical properties. In this dissertation we report the preparation and characterization of water soluble polymer stabilized transition metal(0) (metal= Ni, Co and Ru) nanoclusters and their v catalysis in hydrogen generation from the hydrolysis of sodium borohydride (NaBH4) and ammonia borane (AB) which are the best candidates as chemical hydrogen storage materials for on-board applications. The water soluble polymer stabilized nickel(0), cobalt(0) and ruthenium(0) nanoclusters were prepared by using two different facile methods; (i) the reduction of metal precursors by sodium borohydride in the presence poly(N-vinyl pyrrolidone) (PVP) in methanol solution after 1h reflux, (ii) the in situ generation during the hydrolysis of ammonia borane in the presence of poly(4-styrene sulfonicacid-co-maleic acid) (PSSA-co-MA). The characterization of both type of polymer stabilized transition metal(0) nanoclusters were done by using UV-Visible electronic absorption spectroscopy (UV-Vis), transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and FT-IR techniques. The catalytic activity of PVP stabilized nickel(0), cobalt(0) and ruthenium(0) nanoclusters was tested in the hydrolysis of NaBH4 and AB. The catalytic acitivity of PSSA-co-MA stabilized nickel(0), cobalt(0) and ruthenium(0) nanoclusters was tested only in the hydrolysis of AB in which they were in situ generated. The kinetics of hydrogen generation from both hydrolysis reactions in the presence PVP or PSSA-co-MA stabilized nickel(0), cobalt(0) and ruthenium(0) nanoclusters were studied depending on the polymer to metal ratio, catalyst concentration, substrate concentration and temperature as well as the activation parameters (Arrhenius activation energy (Ea), activation enthalpy (∆H≠) and activation entropy (∆S≠) of both catalytic hydrolysis were calculated from the kinetic data.