Akademik Veri Yönetim Sistemi
Tezin Türü: Doktora
Tezin Yürütüldüğü Kurum: Orta Doğu Teknik Üniversitesi, Mühendislik Fakültesi, Metalurji ve Malzeme Mühendisliği Bölümü, Türkiye
Tezin Onay Tarihi: 2010
Öğrenci: TARIK AYDOĞMUŞ
Danışman: BİLGEHAN ÖGEL
Özet:Porous TiNi alloys (Ti-50.4 at. %Ni and Ti-50.6 at. %Ni) with porosities in the range 21%-81% were prepared successfully applying a new powder metallurgy fabrication route in which magnesium was used as space holder resulting in either single austenite phase or a mixture of austenite and martensite phases dictated by the composition of the starting prealloyed powders but entirely free from secondary brittle intermetallics, oxides, nitrides and carbonitrides. Magnesium vapor do not only prevents secondary phase formation and contamination but also provides higher temperature sintering opportunity preventing liquid phase formation at the eutectic temperature, 1118 °C resulting from Ni enrichment due to oxidation. By two step sintering processing (holding the sample at 1100 °C for 30 minutes and subsequently sintering at temperatures higher than the eutectic temperature, 1118 °C) magnesium may allow sintering probably up to the melting point of TiNi. The processed alloys exhibited interconnected (partially or completely depending on porosity content) open macro-pores spherical in shape and irregular micro-pores in the cell walls resulting from incomplete sintering. It has been found that porosity content of the foams have no influence on the phase transformation temperatures while deformation and oxidation are severely influential. Porous TiNi alloys displayed excellent superelasticity and shape memory behavior. Space holder technique seems to be a promising method for production of porous TiNi alloys. Desired porosity level, pore shape and accordingly mechanical properties were found to be easily adjustable.