Ternary nanocomposites of high density, linear low density and low density polyethylenes

---

Tezin Türü: Yüksek Lisans

Tezin Yürütüldüğü Kurum: Orta Doğu Teknik Üniversitesi, Fen Bilimleri Enstitüsü, Fen Bilimleri Enstitüsü, Türkiye

Tezin Onay Tarihi: 2007

Öğrenci: EGEMEN UÇAR

Danışman: ÜLKÜ YILMAZER

Açık Arşiv Koleksiyonu: AVESİS Açık Erişim Koleksiyonu

Özet:

In this study, the effects of organoclay loading, compatibilizer loading and polyethylene type on the morphology, rheology, thermal properties and mechanical properties of polyethylene/compatibilizer/organoclay nanocomposites were investigated. As compatibilizer, terpolymer of ethylene-methacrylate-glycidyl methacrylate (Lotader® AX8900), as organoclay Cloisite® 15A were used. All samples were prepared by a co-rotating twin screw extruder, followed by injection molding. Considering ternary nanocomposites, highest impact strength results were obtained with 10% compatibilizer plus 2% organoclay; highest yield stress, elastic modulus, flexural strength, flexural modulus were obtained with 5% compatibilizer plus 4-6% organoclay. DSC data indicated that addition of organoclay and compatibilizer did not change the melting point remarkably; on the other hand it affected the crystallinity. The organoclay used had no nucleation effect on polyethylene, and the compatibilizer decreased the crystallinity of the matrix. X-ray diffraction showed that in all ternary nanocomposites and in binary nanocomposite of high density polyethylene with organoclay, layer separation associated with intercalation of the clay structure occurred,. The highest increase of interlayer gallery spacing was obtained with 10% compatibilizer plus 2% organoclay, which were 25%, 28% and 27% for HDPE, LLDPE and LDPE matrices respectively.