Çelik içyapılarının manyetik barkhausen gürültüsü yöntemi ile karakterizasyonu.


Tezin Türü: Yüksek Lisans

Tezin Yürütüldüğü Kurum: Orta Doğu Teknik Üniversitesi, Mühendislik Fakültesi, Metalurji ve Malzeme Mühendisliği Bölümü, Türkiye

Tezin Onay Tarihi: 2006

Tezin Dili: İngilizce

Öğrenci: Kemal Davut

Danışman: CEMİL HAKAN GÜR

Özet:

This aim of this thesis is to examine the possibility of using Magnetic Barkhausen Noise (MBN) technique in characterizing the microstructures of quenched and tempered low alloy steels as well as annealed low carbon steels. To determine the average grain size by MBN, SAE 1010 steel consisting of dominantly ferrite was used. The specimens were slowly cooled in the furnace after austenitizing at different time and temperature variations. By metallographic examination the average ferrite grain size of specimens was determined. The magnetic parameters were measured by a commercial MBN system. With increasing ferrite grain size, the magnetic Barkhausen jumps caused by the microstructure were decreased due to the reduction in grain boundary density per unit volume. A clear relationship has been observed between average grain size and the magnetic Barkhausen noise signals. SAE 4140, 5140 and 1040 steels were used to characterize the microstructures of quenched and tempered specimens. After austenitizing and quenching identically, the specimens were tempered at various temperatures between 200oC and 600oC. Formation of the desired microstructures was ensured by metallographic examinations and hardness measurements. The results show that as tempering temperature increases the Barkhausen activity increases due to the enhancement of domain wall displacement with softening of the martensite. It has been shown that MBN is a powerful tool for evaluating the microstructures of martensitic and annealed steels.