Investigation of the properties of portland slag cement produced by separate grinding and intergrinding methods

---

Tezin Türü: Yüksek Lisans

Tezin Yürütüldüğü Kurum: Orta Doğu Teknik Üniversitesi, Mühendislik Fakültesi, İnşaat Mühendisliği Bölümü, Türkiye

Tezin Onay Tarihi: 2009

Öğrenci: ÇAĞLAR GEVEN

Danışman: İSMAİL ÖZGÜR YAMAN

Özet:

In recent years, there has been a growing trend for the use of industrial by-products in the production of blended cements because of economical, environmental, ecological and diversified product quality reasons. Granulated blast furnace slag, a by-product of the transformation of iron ore into pig-iron in a blast furnace, is one of these materials which is used as a cementitious ingredient. The aim of this study is to investigate the properties of Portland slag cement (CEMII/B-S) by using separate grinding and intergrinding of granulated blast furnace slag and Portland cement clinker. For this purpose, granulated blast furnace slag was used as mineral admixture replacing 30% of the clinker. Clinker and granulated blast furnace slag were ground to four different Blaine fineness values of 3000 cm2/g, 3500 cm2/g, 4000 cm2/g and 4500 cm2/g by intergrinding and separate grinding in a laboratory ball mill. Then, eight Portland slag cement mixes and four Portland cement control mixes were prepared, in order to determine and compare 2-, 7-, 28-, and 90-day compressive and flexural strengths, normal consistencies and setting times. It was found that for the Blaine fineness values of 3000 cm2/g, 3500 cm2/g and 4000cm2/g, the 2-, 7-, 28-, and 90-day compressive strength of the interground Portland slag cements had higher values than the separately ground Portland slag cements. However, for the Blaine fineness values of 4500 cm2/g, separately ground Portland slag cement specimens had slightly higher 2-, 7-, 28-, and 90-day compressive strength values than the interground ones.