Tezin Türü: Yüksek Lisans
Tezin Yürütüldüğü Kurum: Orta Doğu Teknik Üniversitesi, Mühendislik Fakültesi, Metalurji ve Malzeme Mühendisliği Bölümü, Türkiye
Tezin Onay Tarihi: 2007
Tezin Dili: İngilizce
Öğrenci: Onur Aydemir
Danışman: AHMET GEVECİ
Özet:In this study it was aimed to analyse refining processes such as decreasing reducible oxide content of ladle slag with affecting parameters in low carbon aluminum killed grades and for the research Erdemir low carbon steel grades 7112K and 7110K are selected. There was a negative correlation between reducible oxide amount in ladle slag and desulphurization capacity of ladle slag with metal-slag reaction and steel internal cleanliness. To refine these properties of slag, aluminium dross, which was aluminium production discard and has a metallic content around %30-35 was used and after ladle treatment operation, decrease in reducible oxides such as FetO, MnO, SiO2, P2O5 was analysed. After the study it was observed that 653 kg. of converter slag leaked during tapping of steel and SiO2 ve P2O5 content of ladle slag had negligible change after ladle treatment. According to the results, it is observed that initial %10-12 (FetO + MnO) content was reduced to % 4.5-5.0 (FetO + MnO) after ladle treatment with use of aluminium dross. Beside of this, in order to see the effect of this slag reduction on steel cleanliness, low carbon aluminium killed grades were compared with ultra-low carbon aluminium killed grades having (FetO + MnO) content of %16-17 in slag. It was seen that reoxidation of aluminium (loss of dissolved aluminium) during continuous casting for ULC (ultra-low carbon) gradesis 144 ppm but for LC grades it was 94 ppm and it was being expected that ULC steel group would have higher inclusion content after casting.