Self-compacting concrete with high volumes of fly ash

---

Tezin Türü: Doktora

Tezin Yürütüldüğü Kurum: Orta Doğu Teknik Üniversitesi, Mühendislik Fakültesi, İnşaat Mühendisliği Bölümü, Türkiye

Tezin Onay Tarihi: 2006

Tezin Dili: İngilizce

Öğrenci: MUSTAFA ŞAHMARAN

Asıl Danışman (Eş Danışmanlı Tezler İçin): Mustafa Tokyay

Eş Danışman: İsmail Özgür Yaman

Özet:

In this investigation, SCCs were prepared by keeping the total mass of cementitious materials (cement and fly ash) constant at 500 kg/m3, in which 30, 40, 50, 60, and 70% of cement, by weight, was replaced by the high-lime and low-lime fly ash. For comparison, a control SCC mixture without any fly ash was also produced. The fresh properties of the SCCs were observed through, slump flow time and diameter, V-funnel flow time, L-box height ratio, U-box height difference, segregation ratio and the rheological parameters (relative yield stress and relative plastic viscosity). Relations between workability and rheological parameters were sought. Setting times and temperature rise of the SCC were also determined. The hardened properties included the compressive strength, split tensile strength, drying shrinkage and permeation properties (absorption, sorptivity and rapid chloride permeability tests) up to 360 days. The results obtained indicated that it is possible to produce SCC with a 70% of cement replacement by both types of fly ash. The use of high volumes of fly ash in SCC not only improved the workability and permeability properties but also made it possible to produce concretes between 33-40 MPa compressive strength at 28 days.