Tezin Türü: Yüksek Lisans
Tezin Yürütüldüğü Kurum: Orta Doğu Teknik Üniversitesi, Mühendislik Fakültesi, Metalurji ve Malzeme Mühendisliği Bölümü, Türkiye
Tezin Onay Tarihi: 2016
Öğrenci: DOĞA DOĞANAY
Eş Danışman: HÜSNÜ EMRAH ÜNALAN, CEVDET KAYNAK
Özet:In this theses, electrically conductive silver nanowire (Ag NW) filled polylactide (PLA) nanocomposites were fabricated and characterized. Ag NWs/PLA nanocomposite films were fabricated using simple solution mixing method and casted onto glass substrates via doctor blading. Following the obtainment of free standing nanocomposites through peeling off, electrical conductivity of the fabricated nanocomposites, interfacial interactions between Ag NWs and PLA as well as nanocomposite morphology, degree of alignment of Ag NWs, transition temperature and crystallinity among with mechanical performance were investigated. Nanowires showed good dispersion within the PLA matrix. Due to their high aspect ratio (≈150), a percolation threshold of 0.13 vol.% was measured for the nanocomposites. Conductivity of the nanocomposites at the maximum loading (1.74 vol.%) was measured as 27 S/m. It was also found that the transition temperatures of PLA matrix remain the same following the formation of nanocomposites.