Özet:The application of carbon fiber reinforced polymers (CFRP) is one of the effective retrofitting and strengthening methods that is used worldwide and is starting to be used in Turkey as well because they have high strength and high modulus in the fiber direction, have very low coefficient of thermal expansion when compared to concrete and steel and are known not to corrode. Since FRPs are lightweight, their mass can be neglected when compared to concrete and steel. However, before proposing this material as an alternative for strengthening and retrofitting applications their long-term behavior should be understood because they are applied on to concrete by several layers of epoxy-based adhesives, which can be affected by change in humidity, temperature and load. Therefore, behavior of CFRP-strengthened structures in varying temperature and humidity conditions must be investigated. In this dissertation, behavior of CFRP confined cylindrical and prismatic concrete specimens having square cross-section were investigated under sustained compressive loads, dry and wet heating-cooling cycles, and outdoor exposures under direct sunlight, to determine the possible changes in their mechanical properties. Sustained loads were applied as the 40% and 50% of their confined axial load capacity. In addition to the sustained loads, specimens were subjected to 200 heating-cooling cycles between -10°C to 50°C. In order to understand the change in behavior of CFRP confined concrete specimens better, they were divided in six groups. A single effect was investigated in each group. After aging tests mechanical properties of the specimens were recorded via monotonic uniaxial loading. It was observed that temperature cycles had little effect on behavior but sustained loads changed the shape of the axial stress-strain diagram and resulted in a dramatic decrease in ultimate strain. Based on the test results and also using the data of similar studies available in the literature, strength and strain models considering the exposures as independent parameters were established and finally axial stress-strain curve was tried to be predicted.