Synthesis of tin oxide-coated gold nanostars and evaluation of their surface-enhanced Raman scattering activities

Elcı A., Demırtas O., Öztürk İ. M., Bek A., Esenturk E.

JOURNAL OF MATERIALS SCIENCE, cilt.53, ss.16345-16356, 2018 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 53
  • Basım Tarihi: 2018
  • Doi Numarası: 10.1007/s10853-018-2792-4
  • Dergi Adı: JOURNAL OF MATERIALS SCIENCE
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.16345-16356
  • Orta Doğu Teknik Üniversitesi Adresli: Evet

Özet

Tin oxide-coated gold nanostar hybrid nanostructures are prepared by first synthesizing gold nanostars (ca. 400nm), then introducing Na2SnO3 precursor followed by its hydrolysis and formation of a tin oxide layer on nanoparticle surface. The synthesized hybrid structures have been characterized by combination of UV-Vis spectroscopy, transmission electron microscope (TEM), energy-dispersive X-ray studies, scanning electron microscope (SEM), X-Ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. The TEM and SEM analyses showed that gold nanostars have a coating with an approximate thickness of 15nm. The tin (IV) oxide coating on the gold nanostars was identified by XRD and XPS analyses and confirmed by FTIR spectroscopy. Surface-enhanced Raman scattering (SERS) spectroscopy was performed on tin oxide-coated and uncoated gold nanostars with crystal violet as a probe molecule. The SERS studies revealed field enhancement properties of Au nanostars, thus their strong SERS activity remained after tin oxide coating.