Developing a trilayer processing technique for superconducting YBa2Cu3O7-delta thin films by using Ge ion implantation

Creative Commons License

Avci I., Tepe M., Oktem B., Serincan U., Turan R., Abukay D.

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, vol.18, no.4, pp.477-481, 2005 (Peer-Reviewed Journal) identifier identifier

  • Publication Type: Article / Article
  • Volume: 18 Issue: 4
  • Publication Date: 2005
  • Doi Number: 10.1088/0953-2048/18/4/016
  • Journal Indexes: Science Citation Index Expanded, Scopus
  • Page Numbers: pp.477-481


For making trilayer superconducting devices based on YBa2Cu3O7-delta (YBCO) thin film processing, we developed a new technique by employing Ge ion implantation. A YBCO thin film of 150 nm thickness having high c-axis orientation and a transition temperature, T, of 90 K was implanted with 80 keV, 1 x 10(16) Ge ions cm(-2) at room temperature. By the result of TRIM calculation, Ge ions were found to penetrate into the YBCO thin film approximately 60 nm below the surface of the film, thus leaving the lower part of the film as a superconductor. Upon implantation with Ge ions, the implanted upper part of the sample lost its electrical conductivity and diamagnetism while its original crystalline structure was preserved. The implanted ions we found did not alter the overall crystal structure of the YBCO thin film; this allowed us to grow an epitaxial superconducting upper layer of YBCO on top of the implanted area, leaving no need to use any buffer layer. The superconducting properties of the upper layer were similar to those of the pure YBCO base layer with an increased room temperature resistivity and a lowered T-c (88 K). This process provides an effective method for fabrication of a trilayer FITS device structure.