Thermoluminescence study on TlGaSSe layered single crystals

Delice S., HASANLI N.

MODERN PHYSICS LETTERS B, vol.28, no.16, 2014 (SCI-Expanded) identifier identifier

  • Publication Type: Article / Article
  • Volume: 28 Issue: 16
  • Publication Date: 2014
  • Doi Number: 10.1142/s0217984914501334
  • Journal Indexes: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Middle East Technical University Affiliated: Yes


The defect centers in TlGaSSe single crystals have been investigated by performing thermoluminescence (TL) measurements with various heating rates between 0.5 K/s and 1.0 K/s in the temperature range of 10-180 K. The TL spectra, with peak maximum temperatures at 39 K and 131 K, revealed the existences of two defect levels. Curve fitting, initial rise and peak shape methods were used to determine the activation energies of two defect centers. The experimental results also showed that the trapping process was dominated by second-order kinetics for the trap related with low temperature peak while the general order (mixed order) kinetics was dominant for the trap donated to high temperature peak. Furthermore, heating rate dependences and traps distributions were studied for two defect centers separately. Thermal quenching effect dominates the behavior of these defects as the heating rate is increased. Also, quasi-continuous distributions were established with the increase of the activation energies from 16 meV to 27 meV and from 97 meV to 146 meV for the traps associated with the peaks observed at low and high temperatures, respectively.