The effect of Esthetic fibers on impact resistance of a conventional heat-cured denture base resin


Creative Commons License

Dogan O. M. , Bolayir G., Keskin S., Dogan A., Bek B., Boztug A.

DENTAL MATERIALS JOURNAL, cilt.26, ss.232-239, 2007 (SCI İndekslerine Giren Dergi) identifier identifier identifier

  • Cilt numarası: 26 Konu: 2
  • Basım Tarihi: 2007
  • Doi Numarası: 10.4012/dmj.26.232
  • Dergi Adı: DENTAL MATERIALS JOURNAL
  • Sayfa Sayıları: ss.232-239

Özet

This study was conducted to observe the changes in impact resistance of a denture base resin reinforced with five types of fiber. E-glass, polyester, rayon, nylon 6, and nylon 6/6 fibers were cut into 2, 4, and 6 mm lengths and added into the resin at a concentration of 3% by weight. Five test specimens for each formulation, as well as control specimens without fiber, were prepared using a mold including a V-shaped notch with 55 x 10 x 10 mm dimensions. Impact tests were carried out using a Charpy-type tester. Additionally, surfaces of the impact sections were observed under a scanning electron microscope (SEM). Results indicated that impact energy tended to increase with fiber length, and that the highest value was recorded for rayon fiber-reinforced specimens of 6 mm length. E-glass fiber reinforcement produced relatively stable, high values for each length, whereby good interfacial strength between polymer matrix and glass fibers was confirmed by SEM analysis.