Al3+ doped nano-hydroxyapatites and their sintering characteristics


Creative Commons License

Evis Z.

JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, cilt.114, sa.1335, ss.1001-1004, 2006 (SCI İndekslerine Giren Dergi) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 114 Konu: 1335
  • Basım Tarihi: 2006
  • Doi Numarası: 10.2109/jcersj.114.1001
  • Dergi Adı: JOURNAL OF THE CERAMIC SOCIETY OF JAPAN
  • Sayfa Sayıları: ss.1001-1004

Özet

Pure and Al3+ doped nano-hydroxyapatites (HA) were synthesized by a precipitation method to investigate their densification and thermal stability after the air sintering at 1100 degrees C and 1300 degrees C. Second phases were formed after increasing the All, content from 2.5% to 7.5% in HA and increasing the sintering temperature from 1100 degrees C to 1300 degrees C. Al3+ addition into HA resulted in change in the hexagonal lattice parameters from the pure HA. When the sintering temperature was increased from 1100 degrees C to 1300 degrees C, densification was improved, which was verified by SEM micrographs. Al3+ addition resulted in smaller grain size after the sintering at 1300 degrees C.