Influence of Ge content and annealing conditions on the PL properties of nc-Si1-xGex embedded in SiO2 matrix in weak quantum confined regime


TUĞAY E., Ilday S., TURAN R., Finstad T. G.

JOURNAL OF LUMINESCENCE, cilt.155, ss.170-179, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 155
  • Basım Tarihi: 2014
  • Doi Numarası: 10.1016/j.jlumin.2014.06.012
  • Dergi Adı: JOURNAL OF LUMINESCENCE
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.170-179
  • Orta Doğu Teknik Üniversitesi Adresli: Evet

Özet

Fabrication of Si (nc-Si), Ge (nc-Ge), and Si1-xGex (nc-Si1-xGex) nanocrystals embedded in SiO2 matrix is achieved by thermal annealing of magnetron-sputtered thin films. Effects of annealing conditions, namely duration and temperature, as well as Ge content on the photoluminescence properties are investigated. Origin and evolution of the photoluminescence signal in the weak quantum confinement regime are discussed. It is found that photoluminescence signals can be decomposed into four Gaussian peaks originating from Ge-related radiative defects located at the sub-oxide (GeOx), either inside the matrix or at the interface region (peak M), nc-Si1-xGex/SiO2 interface-related localized states (peak I), localized states in the amorphous Si1-xGex bandgap (peak A) and quantum confinement of excitons in small nanocrystals (peak Q). The role of small and large nanocrystals in the photoluminescence mechanism is investigated by varying the mean nanocrystal size from 3 nm to 23 nm (from strong to weak quantum confined regime). Our results demonstrate that the quantum confinement effect in Ge nanocrystals manifests though spectral blueshift due to increase in Ge content. We also propose that the decreasing photoluminescence signal intensity with an increase in Ge content may originate from Ge-related nonradiative P-b centers. (C) 2014 Elsevier B.V. All rights reserved.