Solidification behavior, glass forming ability and thermal characteristics of soft magnetic Fe-Co-B-Si-Nb-Cu bulk amorphous alloys

AYKOL M., AKDENİZ M. V., MEKHRABOV A.

INTERMETALLICS, cilt.19, sa.9, ss.1330-1337, 2011 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 19 Sayı: 9
  • Basım Tarihi: 2011
  • Doi Numarası: 10.1016/j.intermet.2011.05.004
  • Dergi Adı: INTERMETALLICS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.1330-1337
  • Anahtar Kelimeler: Glasses, metallic, Thermal stability, Magnetic properties, Rapid solidification processing, NANOCRYSTALLINE ALLOYS, SUPERHIGH STRENGTH, METALLIC GLASSES, CLUSTERING STAGE, CRYSTALLIZATION, PHASE
  • Orta Doğu Teknik Üniversitesi Adresli: Evet

Özet

The effect of varying Cu content on the bulk glass forming ability (GFA) of (Fe(0.36)Co(0.36)B(0.192)Si-(0.048)Nb(0.04))(100-X)Cu(X) alloys (X = 0, 0.5, 0.75 and 1.0) is revealed by investigating the thermal behaviors and phase competitions upon solidification. The changes in GFA are interpreted in terms of suppression of consecutive solidification reactions via microstructural and thermal features. Instead of the type of the primary crystallization product originating from the prevalent atomic order in the glass or supercooled liquid, precipitation of faceted binary and higher-order pro-eutectic compounds such as (Fe,Co)(2)B and (Fe,Co)NbB from the alloy melt and resulting skewed eutectic coupled zone are correlated with the observed GFA. With the employed centrifugal casting method, the (Fe(0.36)Co(0.36)B(0.192)-Si(0.048)Nb(0.04))(99.25)Cu(0.75) alloy shows the largest critical thickness of 3 mm and the best soft magnetic properties such as 1.58 T saturation magnetization intensity and 11.7 A/m coercivity after annealing. (C) 2011 Elsevier Ltd. All rights reserved.